Influência da espessura nas propriedades de absorção e emissão e na morfologia de filmes automontados de poli(p-fenileno vinileno)

AUTOR(ES)

Piovesan, Erick, Hidalgo, Ángel Alberto, Marletta, Alexandre, Vega, Maria Leticia, Ruggiero, Reinaldo

FONTE

Química Nova

DATA DE PUBLICAÇÃO

2006-10

RESUMO

In this report, we studied the thickness effect on the optical and morphological properties of self-assembled (SA) poly(p-phenylenevinylene) (PPV) films, wich were processed with 5 and 75 layers from a PPV precursor polymer and dodecylbenzenesulfonate, and then, thermally converted at 230 °C. The increase of the film thickness yielded more intense peaks in the vibrational spectral range. The electron-phonon coupling was quantified by the Huang - Rhys factor, that shows the effects on the polymer chain mobility in the interface substrate/polymer. A strong emission anisotropy r=0.57 was observed for the film with 5 layers of thickness decreasing to 0.34 for the film with 75 layers. Finally, the surface topology of the films was measured using Atomic Force Microscopy.

Documentos Relacionados

• Efeito da fotocondução em diodos com camada ativa de derivados de poli(p-fenileno vinileno) (PPV)
• Influência do pH nas propriedades físico-químicas, térmicas e mecânicas de filmes de poli(vinil álcool)/poli(ácido acrílico)/aciclovir
• Influência da adição de plastificante do processo de reticulação na morfologia, absorção de aguá e propriedades mecânicas de filmes de alginato de sódio
• Sintese e caracterização das propriedades eletricas do poli (p-fenileno-CO-2,5-pirazina)
• Desposição de filmes metálicos sobre a poli(Tereflalato de etileno) via Triodo-Magnetron- Sputtering: influência da corrente e das voltagem nas propriedades do filmes