Influence of silane content and filler distribution on chemical-mechanical properties of resin composites

AUTOR(ES)
FONTE

Braz. oral res.

DATA DE PUBLICAÇÃO

02/06/2015

RESUMO

This study investigated the influence of silane concentration and filler size distribution on the chemical-mechanical properties of experimental composites. Experimental composites with silane contents of 0%, 1% and 3% (in relation to filler mass) and composites with mixtures of barium glass particles (median size = 0.4, 1 and 2 μm) and nanometric silica were prepared for silane and filler analyses, respectively. The degree of conversion (DC) was analyzed by FTIR. Biaxial flexural strength (BFS) was tested after 24-h or 90-d storage in water, and fracture toughness, after 24 h. The data were subjected to ANOVA and Tukey’s test (p = 0.05). The DC was not significantly affected by the silane content or filler distribution. The 0% silane group had the lowest immediate BFS, and the 90-d storage time reduced the strength of the 0% and 3% groups. BFS was not affected by filler distribution, and aging decreased the BFS of all the groups. Silanization increased the fracture toughness of both the 1% and 3% groups, similarly. Significantly higher fracture toughness was observed for mixtures with 2 μm glass particles. Based on the results, 3% silane content boosted the initial strength, but was more prone to degradation after water storage. Variations in the filler distribution did not affect BFS, but fracture toughness was significantly improved by increasing the filler size.

Documentos Relacionados