Influence of investment granulometry on the castability and surface roughness of castings obtained with Ni/Cr alloys
AUTOR(ES)
Brisotti, Maria Beatriz, Garcia, Lucas da Fonseca Roberti, Consani, Simonides, Pires-de-Souza, Fernanda de Carvalho Panzeri
FONTE
Materials Research
DATA DE PUBLICAÇÃO
2009-06
RESUMO
The aim of this study was to verify the influence of investment granulometry on the castability and surface roughness of Ni/Cr castings. Four investments were selected for casting according to decreasing order of granulometry: Heat Shock > Micro Fine 1700 > Gilvest HS > Castotal. Castability was verified by means of 40 specimens made with a polyester screen and determined from the number of segments completely filled by the cast alloy. To analyze the roughness, 40 disk-shaped wax patterns were made (15 x 3 mm), and after inclusion in the investments, they were cast and analyzed, before and after polishing (Mitutoyo SJ-201). The measurements were statistically analyzed (1-ANOVA - Tukey - p < 0.05) and it was verified that Heat Shock provided the worst castability with significant difference (p < 0.05) when compared with other investments. This material and Castotal presented similar roughness before and after polishing, with statistically significant difference (p < 0.05) between them and Gilvest and Micro Fine. It was concluded that investments with smaller granulometry provided castings that were more complete, but not smoother.
Documentos Relacionados
- Effect of casting temperature and atmosphere on castability of Ni-Cr alloys: a comparative study with direct flame casting method
- Effect of casting atmosphere on the shear bond strength of a ceramic to Ni-Cr and Ni-Cr-Be alloys
- Microstructural evidence of beryllium in commercial dental Ni-Cr alloys
- Bond strength of three dental porcelains to Ni-Cr and Co-Cr-Ti alloys
- ESTUDO COMPARATIVO ENTRE CINCO LIGAS DE NÃQUEL-CROMO NO TOCANTE A FLUIDEZ E CONSEQÃENTE REPRODUTIBILIDADE