Influence of Gd, Nd and Ce Additions on Microstructures and Mechanical Properties of Ultra-light Dual Phase Mg-9Li-0.4Zr Alloys
AUTOR(ES)
Bao, Lei, Zhang, Zhiqiang, Le, Qichi, Li, Qinxue, Cui, Jianzhong
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
12/04/2016
RESUMO
Effects of various rare-earth elements (RE: Gd, Nd and Ce) additions on microstructures and mechanical properties of ultra-light dual phase Mg-9Li-0.4Zr alloy were investigated. The results indicated that Mg-9Li-5RE-0.4Zr alloys exhibited α-Mg, β-Li and RE-containing intermetallic compound structures. 5 wt.% Gd, Nd and Ce additions enhanced the strength properties of as-extruded Mg-9Li-0.4Zr alloy, but greatly deteriorated the ductility. The final mechanical properties of Mg-9Li-5RE-0.4Zr alloys were 161MPa∼167MPa in ultimate strength, 141MPa∼156MPa in yield strength and 20.8%∼32.5% in elongation. Heat treatment was hardly able to improve the mechanical properties for Mg-9Li-5RE-0.4Zr alloys.
Documentos Relacionados
- The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x = 0, 0.5, 1 and 2 wt%) Alloys
- New Zr-based glass-forming alloys containing Gd and Sm
- Influences of heat treatment on the structure and electrochemical properties of Mg0.9Ti0.1Ni hydrogen storage alloys
- Influence of Small Content Elements Additions on the Glass Forming Ability of Zr-based Bulk Metallic Glasses Alloys
- MICROESTRUCTURAL STABILITY OF AL - 2.4 LI - 1.2 CU - 0.6 MG - 1.12 ZR ALLOY (8090) SUBJECTED TO REGRESSION AND REAGING TREATMENTS