Impact of light-curing time and aging on dentin bond strength of methacrylate- and silorane-based restorative systems
AUTOR(ES)
Catelan, Anderson, Soares, Giulliana Panfiglio, Bedran-Russo, Ana Karina, Lima, Débora Alves Nunes Leite, Marchi, Giselle Maria, Aguiar, Flávio Henrique Baggio
FONTE
Braz. J. Oral Sci.
DATA DE PUBLICAÇÃO
2014-09
RESUMO
AIM: To evaluate the impact of different light-curing times on dentin microtensile bond strength of two restorative systems after 24 h and 6 months of water storage. METHODS: Standardized Class II preparations were performed in 56 freshly-extracted human molars (n = 7), restored with methacrylate- or silorane-based restorative systems, and light-cured using a light-emitting diode at 1390 mW/cm2 by the recommended manufacturers' time or double this time. After storage for 24 h at 37 oC, the teeth were sectioned to yield a series of 0.8-mm thick slices. Each slab was trimmed into an hourglass shape of approximately 0.64 mm2 area at the gingival dentin-resin interface. Specimens were tested using universal testing machine at crosshead speed of 0.5 mm/min until failure, after 24 h and 6 months of storage. Data were statistically analyzed by three-way ANOVA and Tukey's test (α = 0.05). RESULTS: The highest bond strength values were recorded for the groups restored with methacrylate system (p<0.001) as well as for extended light-curing time (p = 0.0034). There was no statistically significant difference between 24 h and 6 months storage on bond strength (p>0.05). CONCLUSIONS: Bond strength was influenced by the material and light-curing time, but the 6-month storage did not affect the bond strength of restorations.
Documentos Relacionados
- Repair Strength in Simulated Restorations of Methacrylate- or Silorane-Based Composite Resins
- Effect of filling technique on the bond strength of methacrylate and silorane-based composite restorations
- Comparison of Silorane and Methacrylate-Based Composites on the Polymerization Heat Generated with Different Light-Curing Units and Dentin Thicknesses
- Influence of pressure application before light-curing on the bond strength of adhesive systems to dentin
- Effect of light-activation with different light-curing units and time intervals on resin cement bond strength to intraradicular dentin