Hg0.8Re0.2Ba2Ca2Cu 3O8.8 thick film produced by Laser Ablation

AUTOR(ES)

Orlando, M. T. D., Rodrigues, V. A., Dias, S. P., Fardin, J. F., Simonetti, D. S. L., Belich, H., Carvalho, C. C., Silva Neto, J. L. da, Yugue, E. S., Werneck, M. M.

FONTE

Journal of Microwaves, Optoelectronics and Electromagnetic Applications

DATA DE PUBLICAÇÃO

2011-06

RESUMO

This paper describes the development of Hg0.8Re0.2Ba2Ca2Cu 3O8.8 thick film prepared with a precursor Ba2Ca2Cu3O5+d thick film, which was layered by Laser Ablation technique on PrBa2Cu3O7 substrate. The precursor thick film was thermally treated under mercury atmosphere using an encapsulate quartz tube technique. DC critical current measurements below T C determined the thick film superconductor current critical density as a function of temperature. The general behavior of the critical current density as a function of temperature confirms that the (Hg,Re)-1223 thick film has junctions type classified as superconducting-insulate-superconducting (SIS). After the critical current test the superconductor thick film has not shown any degradation or stoichiometry loss and its critical temperature has not changed after the test. Taken into account the critical current value of thick film as compared with the bulk sample, it was suggested that the procedure described here can be applied to build most electronic-type applications based on (Hg,Re)-1223 ceramic thick film.

Documentos Relacionados

• Microwave Assisted Synthesis and Sintering of Ba0.5Sr0.5Co0.8Fe0.2O3-δ Perovskite
• Synthesis of the Perovskite-Type BaCe0.8Pr0.05Cu0.15O3-δ via EDTA-Citrate
• Study of the crystal structure of the high Tc superconductor Hg1-xRe xBa2Ca2Cu3O8+δ by using EXAFS, XANES and XRD
• Estudo teórico do comportamento magnético do composto Y0.8Gd0.2Co3
• Produção e caracterização de membranas tubulares finas de Ba0.5Sr0.5Co0.8Fe0.2O3-δ (BSCF) em função do tipo de ligante polimérico empregado