Glass Forming Ability and Mechanical Properties of Zr57.52Co21.24Al9.24Ag12 bulk metallic glass

AUTOR(ES)

Borja Soto, Carlos Ernesto, Figueroa Vargas, Ignacio Alejandro, Lara Rodríguez, Gabriel Ángel, Verduzco Martínez, Jorge Alejandro

FONTE

Mat. Res.

DATA DE PUBLICAÇÃO

10/10/2016

RESUMO

The effect of the partial substitution of Al for Ag in the glass forming ability (GFA) of the Zr57.52Co21.24Al21.24-xAgx (x = 8, 10, 12, and 14 at. %) family alloy are reported and discussed. Cylindrical and conical ingots were obtained using the suction casting technique. It was found that the Zr57.52Co21.24Al9.24Ag12 alloy showed a glassy structure, with a critical glassy diameter, Dc, of 2 mm and ∆Tx = 41 K. The bulk metallic glass Zr57.52Co21.24Al9.24Ag12 alloy was examined using scanning electron microscopy, differential thermal analysis and mechanical compression test. This alloy showed a Young´s modulus (E) of 76.4 GPa and yield strength (σy) of 1.58 GPa. The Glass Forming Ability of the Zr57.52Co21.24Al9.24Ag12 was explained in terms of the topological model of dense packed clusters and kinetic fragility index of the alloy.

Documentos Relacionados

• Microstructural Evolution and Mechanical Properties of Ni57Nb33Zr5Co5 Metallic Glass
• Influence of Small Content Elements Additions on the Glass Forming Ability of Zr-based Bulk Metallic Glasses Alloys
• Crystallization Behavior and Mechanical Properties of Cu-based Bulk Metallic Glass Composites
• Effects of Forming Pores on Mechanical Property of Zr70Cu30 Metallic Glass
• Effect of ion irradiation on mechanical behaviors of Ti40Zr25Be30Cr5 bulk metallic glass