Fundente para Recargue por Soldadura con Arco Sumergido a Partir de Ferrocromo-manganeso y Escoria de la Reducción Simultánea de Cromita y Pirolusita

AUTOR(ES)

Cruz-Crespo, Amado

FONTE

Soldag. insp.

DATA DE PUBLICAÇÃO

24/10/2019

RESUMO

Abstract The obtaining of a flux for hardfacing by Submerged Arc Welding (SAW), using ferrochrome-manganese and slag obtained from the simultaneous carbothermal reduction of chromite and pyrolusite is addressed. The ferrochrome-manganese and the slag were obtained, conceiving that both products satisfy the requirements of the components (alloy system and matrix) of an agglomerated flux for hardfacing. The fusion-reduction process to obtain the alloy and the slag was carried out in a direct current electric arc furnace. The pouring was carried out into water to facilitate the separation and grinding of the cast products. An experimental flux was manufactured, using the obtained alloy and slag. Deposits were obtained by SAW, which were characterized in terms of: chemical composition, microstructure and hardness. It was concluded that the flux obtained from ferrochrome-manganese and slag from the simultaneous carbothermal reduction of chromite and pyrolusite, allows to deposit an appropriate metal for work under abrasion conditions, characterized by significant carbon and chromium contents and a martensitic microstructure predominantly, with hardness of 63 HRc.

Documentos Relacionados

• Optimización de los Parámetros de Soldadura por Arco Sumergido en Acero HSLA: una Aplicación para Manufactura de Tuberías de Conducción de Hidrocarburos
• Comportamiento del tiempo de duración, la frecuencia de los cortocircuitos y la conductividad eléctrica durante el reencendido del arco en la soldadura SMAW (AC) con electrodos E6013
• Cuantificación de la contaminación del gas de protección en procesos de soldadura con arco eléctrico por medio de mediciones de oxígeno en la superficie del material base
• Métodos Ultravioleta Selectivo y de reducción con Hidracina en la determinación del ión nitrato an aguas subterraneas
• Influencia de la temperatura de curado: hidratación y resistencia de pastas de cemento con escoria