Fotoeletrodegradação do corante AO7 utilizando filmes de nanocompósitos de ZnO-TiO2

AUTOR(ES)

Frade, Tânia, Gomes, Anabela, Pereira, Maria Isabel da Silva, Lopes, Ana, Ciríaco, Lurdes

FONTE

Química Nova

DATA DE PUBLICAÇÃO

2012

RESUMO

The Zn-TiO2nanocomposite films were prepared by electrodeposition, using an acidic zinc sulphate solution with TiO2 nanoparticles in suspension. The as-deposited samples have been heated in air at 450 ºC for 6 h. The XRD and SEM analyses pointed out to the metal matrix conversion from Zn to ZnO and a rich morphology of needles-shaped grains. These materials were used on the photoelectrochemical degradation of AO7, which was efficiently degraded, with 40% of color removal, after 2 h period at 1.0 V, under white light irradiation. The apparent first order rate constant of the photoelectrodegradation reaction was 4.12 x 10-3 min-1.

Documentos Relacionados

• Nanocompósitos semicondutores ZnO/TiO2: testes fotocatalíticos
• INFLUÊNCIA DO TRATAMENTO TÉRMICO NO NANOCOMPÓSITO FOTOCATALISADOR ZnO/TiO2
• DEGRADAÇÃO FOTOCATALÍTICA DE CORANTE UTILIZANDO-SE NANOCOMPÓSITO TiO2/ÓXIDO DE
• Células solares de TiO2 sensibilizado por corante
• Fotocatálise do corante vermelho de metila com TiO2 obtido pelo método Pechini