Filme fino de ZrO2 enxertado sobre a superfície de sílica gel: preparação e propriedade de adsorção de Cr(VI)

AUTOR(ES)

Lazarin, Angélica M., Borgo, Claudemir A., Gushikem, Yoshitaka

FONTE

Química Nova

DATA DE PUBLICAÇÃO

2002-05

RESUMO

The present experiment describes an easy procedure for obtaining SiO2/ZrO2 by reacting ZrOCl2 with SiO2 with the following characteristics: S BET = 500 m² g-1 and an average pore diameter of 6 nm. The material obtained presented 1.3 wt% ZrO2 content corresponding to 140 mumol g-1. The average density of ZrO2 onto SiO2/ZrO2 matrix is 2.8x10-11 mol cm-2. The adsorption isotherm for Cr(VI) showed a maximum of adsorption value (200 mumol g-1) at pH 2. The adsorption can be described by the reaction: =Zr(OH)2 + 2HCrO4- + 2H+ [(=Zr(OH2+)2) (HCrO4-)2]. Above the zero point of charge, i.e. pH > 5.5 due to the surface charge inversion, desorption of Cr(VI) occurs according to the reaction: [(=Zr(OH2+)2) (HCrO4-)2] + 6OH- (=ZrO2)2- + 6H2O + 2CrO4(2-).

Documentos Relacionados

• Dispersão de nanopartículas de ZrO2 visando produção de nanocompósitos de ZrO2 em matriz de Al2O3
• Estudo da redução de Cr(VI) por acido nitrico
• Deposição de filmes de ZrO2 modificados sobre substratos metálicos
• Adsorção de Cr(VI) em esferas reticuladas de quitosana: novas correlações cinéticas e termodinâmicas utilizando microcalorimetria isotérmica contínua
• Evaluation of analytical procedures for determination of Cr(III and Cr(VI) in solid samples.