Failure analysis of the polymeric external layer of the umbilical cables. / Análise de falha da camada polimérica externa de cabos umbilicais.

AUTOR(ES)
DATA DE PUBLICAÇÃO

2007

RESUMO

In the present work is proposed a method to establish a failure criterion of the polymeric external layer of umbilical cables used in offshore operations. The proposed method is based on the determination of the increment of the quantity of absorbed water by the polymeric external layer of the cable due to deterioration caused by cyclic loads and the aging process originated by the marine environment. The method proposes to carry out a uniaxial fatigue test on the polymer that composes the external layer of the cable. This test is made simulating the cyclical deformation that the external layer is submitted in the umbilical during the fatigue test done, according to the API 17E standard, during the process of cable homologation. It is also intended to make an artificial aging test in the polymeric external layer simulating the service conditions of the cable in the marine environment. In order to evaluate of the cyclical loads and the sea set aging influence on the properties of the polymer, carry out water absorption test according to the ASTM D 570 standard, traction test according to the ASTM D 638 standard, hardness test according to the ASTM D 2240 standard and observations in an scanning electron microscopy. Finally starting from the mass increment suffered by the polymer in the water absorption test it was estimated the damage in the external layer material of the cable. The results obtained in this work showed that the cyclical loads and marine environment accelerated the degradation process of polymeric external layer of umbilical cable demonstrating the efficiency of the proposed method.

ASSUNTO(S)

failure polímeros (materiais) umbilical cable water absorption fadiga dos materiais cabos umbilicais damage fatigue hdpe imperfeições e falhas dos materiais aging

ACESSO AO ARTIGO

Documentos Relacionados