Factors Affecting Kinetics of Strain Aging in S275JRC Steel
AUTOR(ES)
Bülbül, Ahmet, Kaçar, Ramazan
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
19/12/2016
RESUMO
The materials parameter i.e. microstructure as well as the processing factors i.e. aging time and temperature, the amount of plastic deformation, and residual stresses affecting the kinetic of strain ageing in the S275JRC steel were investigated in detail. For this purpose, 5 % pre-strained steel was aged at 160ºC for different intervals. The ageing behavior was determined for the as-received (AR) and homogenization & normalizing heat treated (H+N heat treated) conditions. The yield stresses before and after aging process and, the hardness values of the aged steels were considered to calculate strain aging progress. It was shown that a noticeable increase in the yield strength, tensile strength and hardness values was observed for aged AR and H+N heat treated specimens. Moreover, the repetitive increase in the yield and ultimate tensile strength was believed to be a result of strain ageing.
Documentos Relacionados
- Factors affecting spore formation in a Candida albicans strain.
- Relevance of Dynamic Strain Aging under Quasi-Static Tension on AISI 304 Stainless Steel
- High Temperature Plastic Instability and Dynamic Strain Aging in the Tensile Behavior of AISI 316 Stainless Steel
- Kinetics of Formation of Fe2B Layers on AISI S1 Steel
- Factors Affecting Nuclear Export of the 60S Ribosomal Subunit In Vivo