Evolution of dendritic patterns during alloy solidification: From the initial instability to the steady state
AUTOR(ES)
Losert, W.
FONTE
The National Academy of Sciences
RESUMO
The evolution of the crystal–melt interface was investigated during directional solidification of a dilute binary alloy, starting at the marginal stability time ti at which the planar interface first becomes unstable. The time delay between ti and the crossover time t0 at which the interface modulation becomes observable was determined experimentally. The interface morphology was analyzed as the cellular pattern appeared, and it was followed through the coarsening phase to the final steady-state dendritic pattern. The relevance of the initial instability for steady-state pattern selection was verified experimentally, and some aspects of the coarsening dynamics were measured and compared with theoretical predictions of Warren and Langer [Warren, J. A. & Langer, J. S. (1990) Phys. Rev. A 42, 3518–3525; Warren, J. A. & Langer, J. S. (1993) Phys. Rev. E 47, 2702–2712].
ACESSO AO ARTIGO
http://www.pubmedcentral.nih.gov/articlerender.fcgi?artid=18438Documentos Relacionados
- Evolution of dendritic patterns during alloy solidification: Onset of the initial instability
- Characterization of the Al-3wt.%Si alloy in unsteady-state horizontal directional solidification
- Predicting Secondary-Dendrite Arm Spacing of the Al-4.5wt%Cu Alloy During Unidirectional Solidification
- Microstructural evolution and mechanical properties of Sn-Bi-Cu ternary eutectic alloy produced by directional solidification
- Evolution of eutectic spacing during unidirectional solidification of Al-Ni alloys