Evaluation of the use of die spacer over the marginal fit of casting copings of Ni-Cr, Ni-Cr-Be and commercially pure Titanium / Avaliação da adaptação marginal de copings metálicos fundidos em ligas de níquel-cromo, níquel-cromo-berílio e em titânio comercialmente puro em função da aplicação de espaçadores
AUTOR(ES)
Natércia Carreira Soriani
DATA DE PUBLICAÇÃO
2008
RESUMO
The purpose of the study was to evaluate the effect of using die spacers on the marginal fit of Ni Cr (Verabond II) (VB II) and Ni-Cr-Be (Verabond) (VB) alloys and commercially pure Titanium (Tritan) (Ti-cp) casting copings by the lost wax technique. Using a metal master die, 135 Resin Added Extra Hard Type IV Stone were obtained for the fabrication of wax patterns in the following conditions: without die spacer (G0), with one die spacer layer (G1); and with two die spacer layers (G2), with fifteen repetitions for each group. Each stone die was waxed and the wax patterns were invested as recommended by the manufacturer. Three wax patterns were embedded in each casting ring, each corresponding to a condition. Each coping, seated to the metal matrix by a Seating Pressure Standardizing Device (SPSD), was taken to the Optic Microscope for the measurement of marginal discrepancy. The obtained data (µm) were submitted to statistical analysis (ANOVA) and Tukey test (p<0.05). There was not statistically significant difference among the materials VB II (93,40) and VB (118,73), and there was statistically significant different to Ti-cp (168,35) . In terms of the die spacer, there was a statistically significant difference among the three conditions (G0=177,31; G1=121,51 e G2=81,66). It was concluded that with two die spacer layers there is less marginal discrepancy.
ASSUNTO(S)
titanium titânio comercialmente puro die spacer espaçadores ligas alternativas cast crown adaptação marginal marginal adaptation ni-cr alloys
Documentos Relacionados
- Effect of the use of die spacer on the marginal fit of copings cast in NiCr, NiCrBe and commercially pure titanium
- Effect of casting atmosphere on the shear bond strength of a ceramic to Ni-Cr and Ni-Cr-Be alloys
- Ataque quimico para promover microrretenções na superficie de ligas metalicas dos sistemas Ni-Cr e Ni-Cr-Be
- Estudo eletroquímico de ligas à base de cobalto-cromo e níquel-cromo
- Pilot study of the adhesion between Ni-Cr alloys and ceramics when prosthetic variables were accomplish