Evaluation of the relationship between the cost and properties of glass ionomer cements indicated for atraumatic restorative treatment
AUTOR(ES)
CALVO, Ana Flávia Bissoto, KICUTI, Ariane, TEDESCO, Tamara Kerber, BRAGA, Mariana Minatel, RAGGIO, Daniela Prócida
FONTE
Braz. oral res.
DATA DE PUBLICAÇÃO
15/12/2015
RESUMO
The aim of this study was to evaluate microshear bond strength (μSBS), water sorption and solubility of glass ionomer cements (GIC) indicated for atraumatic restorative treatment (ART). Cylindrical specimens (6x2.4 mm) were used to test the sorption and solubility of each GIC (n = 5). The specimens were weighed before and after immersion in water and desiccation. For the μSBS test, 60 primary molars were ground to obtain flat surfaces from both enamel and dentin. The teeth were then assigned to the tested GIC (n = 10) groups, namely Fuji IX - FIX, Ketac Molar - KM and Maxxion R – MX. The exposed surfaces were pre-treated with GIC liquid. Polyethylene tubes were placed on the pre-treated surface and filled with one of the GIC. After 24 h, the specimens were submitted to the μSBS test. The failure mode was assessed using a stereomicroscope (400x magnification). The powder to liquid ratio and cost of material were also determined (n = 3). The data were analyzed by ANOVA and Tukey's post hoc test. Linear regression was used to determine the relation between cost and the other variables. Overall, MX showed lower μSBS values (enamel: 3.93 ± 0.38; dentin: 5.04 ± 0.70) than FIX (enamel: 5.95 ± 0.85; dentin: 7.01 ± 1.06) and KM (enamel: 5.91 ± 0.78; dentin: 6.88 ± 1.35), as well as higher sorption and solubility. The regression analyses showed a significant and positive correlation between cost and μSBS in enamel (R2 = 0.62; p < 0.001) and dentin (R2 = 0.43; p < 0.001); and a negative correlation between cost and water sorption (R2 = 0.93; p < 0.001) and solubility (R2 = 0.79; p < 0.001). In conclusion, the materials indicated for ART exhibit distinct physical and mechanical properties; in addition, low-priced materials may interfere with GIC properties.
Documentos Relacionados
- Surface roughness of glass ionomer cements indicated for atraumatic restorative treatment (ART)
- Mechanical performance of encapsulated restorative glass-ionomer cements for use with Atraumatic Restorative Treatment (ART)
- In vitro and in vivo evaluations of glass-ionomer cement containing chlorhexidine for Atraumatic Restorative Treatment
- Mechanical and optical properties of conventional restorative glass-ionomer cements - a systematic review
- Microhardness of glass ionomer cements indicated for the ART technique according to surface protection treatment and storage time