Evaluation of hydrogen-Induced cracking resistance of the In625 laser coating system on a C-Mn steel substrate

AUTOR(ES)

Trindade, Vicente Braz, Almeida, Natália Chaves, Cândido, Luiz Cláudio, Faria, Geraldo Lúcio de, Lima, Milton Sergio Fernandes de

FONTE

REM, Int. Eng. J.

DATA DE PUBLICAÇÃO

2017-06

RESUMO

Abstract The corrosion of C-Mn steels in the presence of hydrogen sulfide (H2S) represents a significant challenge to oil production and natural gas treatment facilities. The failure mechanism induced by hydrogen-induced cracking (HIC) in a Inconel 625 coating / C-Mn steel has not been extensively investigated in the past. In the present work, an API 5CT steel was coated with In625 alloy using laser cladding and the HIC resistance of different regions, such as the coating surface, the substrate and HAZ, were evaluated. SEM observations illustrated that all HIC cracks were formed at the hard HAZ after 96h of exposure. No HIC cracks were observed in the substrate and the In625 coating after the same exposure duration. Pitting was recorded in the substrate caused by non-metallic inclusion dissolving.

Documentos Relacionados

• Microstructural Evolution of Ultra Fine Grained C-Mn Steel Warm Rolling and Intercritical Annea
• Effect of the Chemical Homogeneity of a Quenched and Tempered C-Mn Steel Pipe on the Mechanical Properties and Phase Transformations
• Caracterização da temperabilidade de um aço C-Mn microligado ao boro, através de dilatometria e curvas de transformações de fases por resfriamento contínuo.
• Soldagem FHPP - processo e metalurgia nas transformações das fases de um aço C-Mn
• Comportamento de Juntas Soldadas de Aço C-Mn Obtidas Pelo Processo GMAW-RE com Eletrodo Rotativo