Evaluation of Co-Ni/SiC Nanocomposite Coating Obtained by Electrodeposition on the Corrosion Resistance of API 5L X80 Steel
AUTOR(ES)
Pereira, Roseana Florentino da Costa, Oliveira, Edkarlla Sousa Dantas de, Vieira, Magda Rosângela Santos, Lima, Maria Alice Gomes de Andrade, Urtiga Filho, Severino Leopoldino
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
29/06/2017
RESUMO
Co-Ni/SiC nanocomposite coatings were obtained by codeposition of SiC nanoparticles in a bath with nickel and cobalt, using API 5L X80 as the substrate. The influence of cathodic current density on deposit properties was investigated. Measurements of electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization (PP) were performed in 3.5 wt% NaCl solution to investigate a corrosion performance. The morphology and chemical analysis of the surfaces were analyzed by scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS) and related with micro-hardness and X-ray diffraction (XRD). The results indicate which composite coatings have acicular morphology, with higher micro-hardness values than those found for the carbon steel substrate. The Co-Ni/SiC coating increased the corrosion potential and the resistance to polarization, which resulted in lower corrosion rates than those obtained without uncoated steel.
Documentos Relacionados
- A Comparative Investigation of the Corrosion Resistance and HIC Suceptibility of API 5L X65 and API 5L X80 Steels
- Analysis of the corrosion scales formed on API 5L X70 and X80 steel pipe in the presence of CO2
- CURVAMENTO POR INDUÇÃO DE TUBO DA CLASSE API 5L X80
- Corrosion Behavior of API 5L X80 Steel in the Produced Water of Onshore Oil Recovery Facilities
- Evenmatched FCAW process in API 5L X80 steel welded joint