Evaluation of Aqueous Coffee Husks Extracts as a Corrosion Inhibitor of 1020 Carbon Steel in 1 mol L-1 HCl Solution
AUTOR(ES)
Ramos, Samantha Alcântara Fernandes
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
09/12/2019
RESUMO
Corrosive processes in acidic medium reduce the performance and durability of metallic materials, causing problems to several industries. Corrosion inhibitors are commonly used to decrease these effects. As these inhibitors must be ecologically friendly currently, this work evaluated the anticorrosive effect of natural extracts of coffee husks (Coffea arabica L.) in the protection of carbon steel in 1 mol L-1 HCl solution. Extractions were performed using water as the extraction solvent. The polyphenols content increased with the extraction temperature, and the extracts were produced using 100 ºC. Extract concentrations of 10, 20 and 30 % v/v were analyzed as inhibitors for carbon steel in acid medium, using weight loss and electrochemical tests, as well as scanning electron microscopy. There was an increase in the inhibition efficiency as the extract concentration increased, reaching values around 97 % using 30 %v/v of extract for the weight loss tests.
Documentos Relacionados
- Barley Agro-industrial Residues as Corrosion Inhibitor for Mild Steel in 1mol L-1HCl Solution
- Roasted Coffee Extracts as Corrosion Inhibitors for Mild Steel in HCL Solution
- Aqueous Extracts of the Castor Beans as a Corrosion Inhibitor of Mild Steel in HCl Media
- Evaluation of the anticorrosion performance of peel garlic extract as corrosion inhibitor for ASTM 1020 carbon steel in acidic solution
- Ação inibidora de extratos da semente do mamão papaia na corrosão do aço-carbono 1020 em HCL 1 mol L-1