Esfoliação e hidratação da caulinita após intercalação com uréia

AUTOR(ES)

Gardolinski, José E., Wypych, Fernando, Cantão, Maurício P.

FONTE

Química Nova

DATA DE PUBLICAÇÃO

2001-12

RESUMO

Well-ordered Georgia kaolinite (Kga-1b) obtained from the source Clay Repository of the Clay Minerals Society (USA) was intercalated with urea using grinding procedures. To achieve complete intercalation 20% of urea (in weight) was used, producing Al2Si2O5(OH)4 (N2H4CO)0,86 with an interplanar basal spacing of 1,08nm. After washing with water under ultrasound stirring at 363K, urea was completely removed and kaolinite was partially exfoliated. After drying under air, the material was converted to hydrated kaolinite with the composition Al2Si2O5(OH)4 (H2O)0,64 and an interplanar basal spacing of 0,84nm. In this compound, water molecules positioned between the layers of the silicate can be removed after calcination at 573K, regenerating structurally disordered kaolinite.

Documentos Relacionados

• Hexaniobato lamelar: Estudos de esfoliação e intercalação"
• Experimentos de intercalação para alteração morfológica da caulinita presente em rejeitos de mineração de ferro
• Adsorção de nitrato em caulinita a partir de rejeito de caulim modificado com uréia
• Intercalação e funcionalização da brucita com ácidos carboxílicos
• Avaliacao da qualidade fisiologica de sementes de soja, apos o processo de hidratacao-desidratacao e envelhecimento acelerado.