"Envelhecimento artificial acelerado - Influência na alteração de cor e rugosidade superficial de resinas indiretas" / Artificial accelerated aging - Changes in color and surface roughness of indirect resins

AUTOR(ES)
DATA DE PUBLICAÇÃO

2005

RESUMO

This study had the aim of assessing in vitro color change and surface roughness of three brands of new generation indirect resins, after being submitted to accelerated aging process. Twelve specimens were constructed (15 mm diameter and 2 mm width) for the resins: Artglass (Heraeus Kulzer), Solidex (Shofu), Targis (Ivoclar Vivadent) which were finished and polished with the disks Sof-Lex - 3M. The first measurements for the roughness and spectrophotometer colorimeter tests were performed, respectively, with the Surfcorder Profilometer SE 1700 (Kosakalab) and Spectrophotometer PCB 6807 (BYK GARDNER), which uses the scale CIE L*a*b* for color determination. The samples were submitted to the accelerated artificial aging process for 384 hours, and then submitted once again to the process of color and roughness reading. Color stability was determined by the difference (ΔE) between coordinates L*, a*, and b* obtained from the samples before and after aging. The results were submitted to ANOVA (Tukey) and showed that all resins presented color changes with no statistical significance (p>0.05). Solidex resin showed the highest value of color change (ΔE = 4.31), and a roughness pattern (Ra= 0.079) statistically different from the resins Art-Glass (Ra=0.141) and Targis (Ra=0.124) (p<0,001). Conclusion: All resins showed color change and an increase of roughness after artificial accelerated aging. Solidex resin showed the highest color change and the lowest roughness after accelerated aging.

ASSUNTO(S)

cor rugosidade surface roughness resinas indiretas espectrofotometria artificial accelerated aging color indirect resins envelhecimento acelerado

ACESSO AO ARTIGO

Documentos Relacionados