Eletrodegradação de Ponceau 2R utilizando ânodos dimensionalmente estáveis e Ti/Pt

AUTOR(ES)

Ribeiro, Francisco Wirley Paulino, Oliveira, Sâmeque do Nascimento, Lima-Neto, Pedro de, Correia, Adriana Nunes, Mascaro, Lúcia Helena, Matos, Roberto de, Souza, Ernesto Chaves Pereira de, Lanza, Marcos Roberto de Vasconcelos

FONTE

Quím. Nova

DATA DE PUBLICAÇÃO

2013

RESUMO

This paper reports the electrochemical degradation of the azo dye Ponceau 2R under galvanostatic electrolysis in the 1 to 200 mA cm-2 range at room temperature using dimensionally-stable anodes of oxygen (DSA-O2), chlorine (DSA-Cl2) and a titanium electrode of platinum coated with platinum oxide (Ti/Pt). The methodology applied was efficient for removing the color of the Ponceau 2R and the highest percentage removal of total organic carbon was obtained at 200 mA cm-2. Despite not having been observed complete mineralization, approximately80% removal of aromatic rings was estimated, resulting in drastic reduction of toxicity of the sample.

Documentos Relacionados

• Influência das condições de resfriamento sobre as propriedades superficiais e eletroquímicas de anodos dimensionalmente estáveis
• Espectroscopia de impedância eletroquímica aplicada ao estudo das reações heterogêneas em ânodos dimensionalmente estáveis
• Production and charactization of doped Ti-Pt/β-PbO2 electrodes and their use in the electrochemical treatment of simulated wastewaters
• A Cytogenetic Analysis of the Punch-Tudor Region of Chromosome 2r in Drosophila Melanogaster
• Fotodestruição de compostos potencialmente toxicos utilizando TiO2 e luz solar