Electrophoretic deposition of BaTi0.85Zr0.15O3 nanopowders
AUTOR(ES)
Antonelli, Eduardo, Silva, Ronaldo Santos da, Bernardi, Maria Inês Basso, Hernandes, Antonio Carlos
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
29/07/2013
RESUMO
The present study reports the results of thick films (20-130 µm) produced through electrophoretic deposition of BaTi0.85Zr0.15O3 (BTZ) nanometric powders synthesized by the Pechini's method. The BTZ powderscalcined at 600°C/2h presented a single crystalline phase with an average particle size of ~20nm. To thick films deposition, a stable suspension of acetylacetone (Acac) and ethanol (EtOH)was prepared and the powder was deposited on platinum substrates. The viscosity of BTZ powders suspensions as a function of operational pH (OpH)was measured and the reactions between nanoparticles and the media were discussed. A milling process was used to deagglomerate the powders and it had a great influence in the suspension stability and deposition of thick films. Dense and crack-free thick films were obtained after sintering at 1220 °C/1h. The dielectric properties results, comparable with those of bulk BTZ ceramics, suggested potential applications of the EPD process for the deposition of ferroelectric/piezoelectric thick films.
Documentos Relacionados
- Electrophoretic deposition of Ba(Ti0.85Zr0.15)O3 nanoparticles to fabrication of laser sintered ferroelectrics thick films
- Sinterização de filmes espessos de Ba(Ti0,85Zr0,15)O3 por varredura laser
- Microestrutura e condutividade elétrica em Ce0,85Y0,15-xRxO2-delta (R=Pr, Tb)
- Ga Dopant Induced Band Gap Broadening and Conductivity Enhancement in Spray Pyrolysed Zn0.85Ca0.15O thin Films
- Microstructure and Dielectric Behavior of Ytterbium Doped BaZr0.1Ti0.9O3 Ceramics