Elaboración de recubrimientos cerámicos mediante proyección térmica por combustión a partir de residuos sólidos industriales

AUTOR(ES)

Restrepo, E., Vargas, F., López, M., Cardona, R., Duarte, G.

FONTE

Matéria (Rio J.)

DATA DE PUBLICAÇÃO

2012

RESUMO

Ceramic coatings were elaborated onto carbon steel substrates by oxy-fuel thermal spraying process from catalysts waste used in petroleum refining. The adhesion and micro-hardness Vickers were evaluated according to ASTM C633-01(2008) and ASTM C1327-08 standards respectively, with adhesion values varying between 2,9 and 17,7 MPa and values of microhardness Vickers between 5,4 and 8 GPa. The results obtained indicate that these coatings could be used in industrial applications, mainly in components requiring resistance to wear and thermal shock or high temperatures, at a low cost due to reuse of solid waste as raw materials in the production of coatings, and giving a technological solution to environment problems produced by these catalysts waste.

Documentos Relacionados

• Espumas vítreas produzidas a partir de resíduos sólidos
• Isolantes térmicos produzidos a partir de resíduos sólidos industriais
• Estudio de la estructura y las propiedades mecánicas en un recubrimiento de circona estabilizada con 8% en mol de itria elaborado por proyección térmica por plasma a partir de suspensiones
• Produção e caracterização de espumas vitrocristalinas a partir de resíduos sólidos
• Residuos sólidos industriais: uma fonte alternativa na elaboração de materiais cerâmicos de baixa densidade