Effects of pre-wetting aggregate on the properties of mortars made with recycled concrete and lightweight aggregates
AUTOR(ES)
Jochem, Lidiane Fernanda
FONTE
Matéria (Rio J.)
DATA DE PUBLICAÇÃO
10/06/2019
RESUMO
RESUMO Este artigo buscou verificar a substituição parcial do agregado natural, areia (NA) por agregado de concreto reciclado (RCA) ou agregado leve (LWA) em argamassas, sob a hipótese que agregados pré-molhados produziriam melhoras nas propriedades da argamassa. Para isso, avaliou-se as propriedades das argamassas no estado fresco, como massa específica, teor de ar incorporado, consistência e calor de hidratação, bem como as propriedades no estado endurecido, como massa específica, resistência à compressão e à flexão, e instabilidade dimensional, com 0% e 100% de saturação. Os resultados mostram que as argamassas preparadas com agregado natural (75%) e agregado de concreto reciclado (25%) possuem propriedades semelhantes às argamassas preparadas com apenas agregado natural (100%) e que a pré-molhagem dos agregados não influenciou significativamente as propriedades das argamassas. Assim, constatou-se que, a substituição parcial do agregado natural por agregado de concreto reciclado é uma alternativa viável para a produção de argamassa.ABSTRACT This paper examines the suitability of partially replacing natural aggregate, sand, (NA) with recycled concrete aggregate (RCA) or lightweight aggregate (LWA) in mortars, under the hypothesis that pre-wetting aggregates would produce improvement in mortar properties. Fresh mortar properties such as density, entrained air content, consistency and heat of hydration, as well as hardened mortar properties such as dry density, compressive and flexural strength, and dimensional instability at 0% and 100% saturation were determined. The results show that mortars made with natural aggregate (75%) and recycled concrete aggregate (25%) have similar properties to mortars made with only natural aggregate (100%) and that pre-wetting the aggregates does not influence the properties of mortars significantly. Therefore, partial replacement with recycled concrete aggregate is a viable alternative for producing mortar.
Documentos Relacionados
- Properties of high-workability concrete with recycled concrete aggregate
- Influence of the moisture content on the dynamic modulus of elasticity of concrete made with recycled aggregate
- Mechanical characterization using optical fiber sensors of polyester polymer concrete made with recycled aggregates
- Experimental investigation on the effects of recycled aggregate on fracture behavior of polymer concrete
- Technological properties of a self-bloating clay and expanded-clay aggregate for the production of lightweight concrete