Effects of modeling liquid/resin and polishing on the color change of resin composite

AUTOR(ES)
FONTE

Braz. oral res.

DATA DE PUBLICAÇÃO

18/08/2016

RESUMO

Abstract Modeling liquids/resins have been used to build up resin composite (RC) restorations, although there is a lack of information regarding their effects on the color stability of the latter. Therefore, the purpose of the present study was to evaluate the effects of the presence of modeling liquid between layers of RC and the finishing/polishing state of the material on color change in specimens exposed to red wine staining over time. Specimens were prepared by placing four increments (±0.5 mm thick) of RC (Filtek™ Z350 XT, 3M ESPE) into molds; half of which were prepared by applying modeling liquid (Scotchbond™ Multi-Purpose™ Adhesive, SBMP, 3M ESPE) between the layers of RC, whereas the other half were prepared without SBMP (control). Light-activation was performed after application of the final RC layer using a light-emitting diode (Radii, SDI) curing unit with an irradiance of 900 mW/cm2 for 20 s. Each group was divided according to the surface finishing protocol (n = 7): nothing (non-polished) or polishing with Sof-Lex™/diamond paste (polished). Initial colors of the specimens were evaluated with a digital spectrophotometer and the CIEL*a*b* color system. The specimens were stored in wine (37°C) for 12 months, and the color measurements were reassessed after 4, 6, and 12 months of storage. Scanning electron microscopy (SEM) analysis was performed at the end. Data were analyzed using ANOVA and Tukey’s test (α = 5%). The presence of SBMP resulted in lower overall color change of the RC as compared with the control. The non-polished specimens exhibited a significantly higher color change than the polished specimens. SEM images corroborated the previous findings. In summary, the use of modeling liquid between layers of RC shows potential for application to reduce or delay the staining process of RC over time. Moreover, polishing is essential to provide increased color stability of the RC restoration.

Documentos Relacionados