Effect of Ti and Nb Additions on the Formation of Craters for IF Steel Galvanneal Coatings
AUTOR(ES)
Breno Torezani Storch
DATA DE PUBLICAÇÃO
2009
RESUMO
Interstitial Free steels feature alloying elements present in an ultra low C matrix that account for C stabilization and consequently a high number of C free interstitials in a ferrite matrix that give these steels the ideal texture, low yield point, favorable plastic strain ratios, high elongation and n-value necessary for an ideal performance on forming press, drawing and stamping operations especially for automotive body part applications. This Masters thesis indicates that Ti-stabilized IF steel substrates are more reactive than dual-stabilized IF steel substrates probably due to the presence of islands of Nb oxides at the interface between the steel substrate and the GA coating. These Nb oxides may block the Fe-Zn interdiffusion along the ferrite grain boundaries. Hence, higher reactivity rates for Ti-stabilized IF steel grades mean that this substrate is more prone than a dual-stabilized IF steel to the formation of outbursts and consequently the formation of craters, which are morphologically characterized as clusters of outbursts, whose formation mechanisms are based on capillarity effects accounting for amounts of liquid Zn being drained away from these spots. Besides, this work has also explored the typical chemistry and morphology features of craters on top of dark and light streaked areas on GA coatings, showing that there are d crystals on the bottom of craters on light streaked areas, whereas G phase was found on the bottom of craters on dark streaked areas. Also, it turns out that craters on dark streaked regions are deeper than those on light streaked areas. On top of that, the crater coverage on dark streaked regions is larger than on light streaked areas.
ASSUNTO(S)
1. aços - teses. 2. galvanização - teses. 3. crateras - teses. 4. titânio - teses. 5. nióbio - teses. i. universidade federal de ouro preto. ii. título engenharia de materiais e metalurgica
ACESSO AO ARTIGO
http://www.tede.ufop.br/tde_busca/arquivo.php?codArquivo=427Documentos Relacionados
- Effect of TiC Particles Concentration on Microstructure and Properties of Ni-TiC Composite Coatings
- Efeito da adição de oxigênio na estabilidade e metaestabilidade de fases em ligas Ti-Nb aplicadas como biomaterial
- Effect of the Incorporation of Micro and Nanocellulose Particles on the Anticorrosive Properties of Epoxy Coatings Applied on Carbon Steel
- The Effect of Immersion Time and Immersion Temperature on the Corrosion Behavior of Zinc Phosphate Conversion Coatings on Carbon Steel
- The effect of polarisation on the electrochemical behavior of Ti-13Nb-13Zr alloy