Effect of Rolling in the Recrystallization Temperature Region Associated with a Post-Heat Treatment on the Microstructure, Crystal Orientation, and Mechanical Properties of API 5L X70 Pipeline Steel

AUTOR(ES)

Masoumi, Mohammad, Silva, Cleiton Carvalho, Abreu, Hamilton Ferreira Gomes de

FONTE

Mat. Res.

DATA DE PUBLICAÇÃO

08/12/2016

RESUMO

In order to improve the mechanical properties of API X70 pipeline steel, a rolling schedule in the recrystallization temperature region associated with a post heat treatment was proposed. Optical and scanning electron microscopy, electron backscattered diffraction, hardness, and tensile tests were carried out to show the effects of microstructure and crystallographic orientation on the final mechanical properties. The normalized hot-rolled sample and the sample subjected to hot-rolling followed by quenching and consequent tempering at 700 °C exhibited an excellent combination of yield strength and elongation. This was attributed to the recrystallized ferrite microstructure and tempered martensite with martensite-austenite constituent dispersion, respectively. In addition, the development of (112)[1̅1̅1] and (111)[101̅] texture components and the high fraction of low angle boundaries have a significant effect on the improvement of the mechanical properties.

Documentos Relacionados

• Microstructure and Properties of Nickel-based C276 Alloy Coatings by PTA on AISI 316L and API 5L X70 Steel Substrates
• Avaliação da tenacidade à fratura de aço API 5L X70 utilizado na fabricação de dutos transportadores de gás e petróleo
• Efeito da temperatura sobre a medição de tensão por ondas Lcr em aços API 5L X70
• The Effect of Post-Heat Treatment in MDF Panels
• Estudo dos processos de corrosão de aços API 5L X70 em contato com alguns dos solos do Brasil