Effect of Quenching Rate and Pre-strain on the Strain Ageing Behaviors of 7075 Aluminum Alloys

AUTOR(ES)

Kaçar, Ramazan, Güleryüz, Kemal

FONTE

Mat. Res.

DATA DE PUBLICAÇÃO

2015-04

RESUMO

The mechanical properties of aluminum alloys are strongly dependent on the thermo-mechanical process so, the strain ageing behavior of 7075 Al-alloy was investigated in this study. A set of test pieces was solution heat treated at 480 °C for 2 h, water quenched (SHTWQ) then pre-strained for 8% in tension. The test samples were aged at 140 °C for 0.5, 1, 2, 3, 4, 6, 8, 10, 12, 24, 48, 72 and 96 h in a furnace. The other set of test samples were solution heat treated at 480 °C for 2 h, quenched in sand (SHTSQ) then pre-strained for 8% in tension. They were also aged at 140 °C for same intervals. The effect of strain ageing, on the mechanical properties of Al-alloy, was investigated by mean of hardness, and tensile tests. The results shown that, the quenching rate after solution heat treatment, ageing time and temperature, as well as pre-strain, play a very important role in the precipitation-hardening associated with ageing process of the 7075 Al-alloy.

Documentos Relacionados

• Effects of Aging Temperature, Time, and Pre-Strain on Mechanical Properties of AA7075
• Effects of Pre-Strain on the Evolution of Microstructure and Strain Hardening of Extruded Az31 Magnesium Alloy
• Effect of porosity on the tensile properties of low ductility aluminum alloys
• Study on Effect of EAFD Particulate Reinforcement in AA7075 Aluminum Matrix Composites
• On the effect of interrupted ageing (T6I4) on the mechanical properties of AA6351 and AA7050 alloys