Effect of PVA Concentration on Structure and Performance of Precipitated Iron-Based Catalyst for Fischer-Tropsch Synthesis
AUTOR(ES)
Ma, Cailian, Dong, Guanghua, Liu, Xia, Chen, Jiangang
FONTE
J. Braz. Chem. Soc.
DATA DE PUBLICAÇÃO
2017-08
RESUMO
Fe2O3 catalysts were prepared by co-precipitation method with the assistance of polyvinyl alcohol (PVA) for Fischer-Tropsch synthesis. Effects of PVA concentration on structure and performance of the catalyst were investigated in a fixed reactor at 230-310 °C, 1.5 MPa, 2000 h-1, and syngas H2/CO = 2.0. The catalysts were characterized by N2 adsorption, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), H2 or CO temperature-programmed reduction (TPR) and H2 temperature-programmed desorption (H2-TPD), Fourier transform infrared (FTIR) spectra and thermogravimetric analysis (TGA). It was found that there was strong interaction between Fe and PVA, which controlled the structure of the catalyst. Among the catalysts investigated, the catalyst prepared with 15 wt.% PVA exhibited better catalytic performance due to the dispersion of iron oxides and the formation of the more active phase on the catalyst. Meanwhile, this catalyst showed the high selectivity to heavy hydrocarbons and satisfactory thermal stability.
Documentos Relacionados
- Effect of K promoter on the structure and catalytic behavior of supported iron-based catalysts in fischer-tropsch synthesis
- Surfactant-Assisted Preparation of FeCu Catalyst for Fischer-Tropsch Synthesis
- Efeito da VariaÃÃo de LÃtio em Catalisadores de Ferro tendo PotÃssio e Cobre como Promotores para a SÃntese Fischer-Tropsch
- Análise termodinâmica de processos de reforma do metano e da síntese Fischer-Tropsch
- Desenvolvimento de um novo catalisador monolítico à base de nanofibras de carbono para a produção de combustíveis limpos através da síntese de Fischer-Tropsch