Effect of High Energy Milling Time of the Aluminum Bronze Alloy Obtained by Powder Metallurgy with Niobium Carbide Addition
AUTOR(ES)
Dias, Alexandre Nogueira Ottoboni, Silva, Aline da, Rodrigues, Carlos Alberto, Melo, Mírian de Lourdes Noronha Motta, Rodrigues, Geovani, Silva, Gilbert
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
10/04/2017
RESUMO
The aluminum bronze alloy is part of a class of highly reliable materials due to high mechanical strength and corrosion resistence being used in the aerospace and shipbuilding industry. It's machined to produce parts and after its use cycle, it's discarded, but third process is considered expensive and besides not being correct for environment reasons. Thus, reusing this material through the powder metallurgy (PM) route is considered advantageous. The aluminum bronze chips were submitted to high energy ball milling process with 3% of niobium carbide (NbC) addition. The NbC is a metal-ceramic composite with a ductile-brittle behaviour. It was analyzed the morphology of powders by scanning electron microscopy as well as particle size it was determined. X ray diffraction identified the phases and the influence of milling time in the diffractogram patterns. Results indicates that milling time and NbC addition improves the milling efficiency significantly and being possible to obtain nanoparticles.
Documentos Relacionados
- Comparative analysis of niobium and vanadium carbide efficiency in the high energy mechanical milling of aluminum bronze alloy
- Evaluation of the milling efficiency increase of AISI 52100 steel using niobium carbide addition through high energy ball milling
- Study of the AISI 52100 Steel Reuse Through the Powder Metallurgy Route Using High Energy Ball Milling
- Synthesis and Characterization of Niobium Carbide with Copper Addition Obtained Via Gas Solid Reaction
- Nanostructured MgH2 obtained by cold rolling combined with short-time high-energy ball milling