Effect of Fluoride-containing Mouthrinses on the Translucence of Resin Modified Glass Ionomer Cements
AUTOR(ES)
Garcia, Patrícia Petromilli Nordi Sasso, Corona, Silmara Aparecida Milori, Dibb, Regina Guenka Palma, Chimello, Daniela Thomazatti, Catirse, Alma Blásida Elizaur, Freitas, Emaneula Maurício
FONTE
Materials Research
DATA DE PUBLICAÇÃO
2002-10
RESUMO
The aim of this in vitro study was to assess the effect of different fluoride-containing mouthrinses on the translucence of resin-modified glass ionomer cements, as a function of the restorative material used, the fluoride-containing solution employed and the time of immersion. Disks were prepared (10 mm × 2 mm) with the modified glass ionomer cements Vitremer (3M) and Fuji II LC (GC Co.), and immersed in three fluoride-containing solutions: Fluordent Reach (Johnson & Johnson), Fluorgard (Colgate-Palmolive) and Oral B (Gillette do Brasil Ltda). Translucence was measured with electrophoresis equipment (JOUAN) after different immersion times. The results obtained were submitted to ANOVA and Tukey's test, and a statistically significant decrease was observed in the translucence of the materials after immersion in the fluoride-containing solutions. Fuji II LC demonstrated the lowest alteration in translucence, independently of the solution employed. Fluorgard was the fluoride-containing mouthrinse that promoted the highest alteration. It can be concluded that the fluoride-containing mouthrinses influenced the translucence of the resin-modified glass ionomer cements.
Documentos Relacionados
- Effect of fluoride-containing desensitizing agents on the bond strength of resin-based cements to dentin
- Effect of fluoride-containing solutions on the surface of cast commercially pure titanium
- Cariostatic effect of fluoride-containing restorative materials associated with fluoride gels on root dentin
- Fluoride release and uptake in enhanced bioactivity glass ionomer cement (“glass carbomer™”) compared with conventional and resin-modified glass ionomer cements
- Effect of light curing unit on resin-modified glass-ionomer cements: a microhardness assessment