Effect of Aluminium Addition on the Magnetic Properties of a Semi-Processed Electrical Steel

AUTOR(ES)

Marra, Kleiner Marques, Marra, Lívia Carneiro, Buono, Vicente Tadeu Lopes

FONTE

Mat. Res.

DATA DE PUBLICAÇÃO

12/09/2016

RESUMO

Aluminum is often added to electrical steels since this element causes improvement of the magnetic properties. However the addition of aluminum is usually limited to 0.30 wt%1. Therefore, this work aimed at evaluating the influence of higher levels of aluminum in the magnetic properties of semi-processed steels. To accomplish this, four types of steel were produced in laboratory with different aluminum contents (0.10, 0.30, 0.60 and 1.0 wt%). Carbon, manganese and silicon concentrations were kept constant. It was observed that an increased aluminum content caused reduction of the magnetic core loss, especially of the eddy current component. However, the magnetic permeability virtually wasn't influenced by aluminum concentration.

Documentos Relacionados

• Avaliação da influência da temperatura e ponto de orvalho no recozimento final de aços elétricos semiprocessados e totalmente processados
• Effect of the Annealing Temperature on the Structure and Magnetic Properties of 2% Si Steel
• The Effect of Co and Zn Addition on Densification and Electrical Properties of Ceria-Based Nanopowders
• Effect of Cross-Rolling on Microstructure, Texture and Magnetic Properties of Non-Oriented Electrical Steels
• The effect of acetone addition on the properties of epoxy