Efeito do protocolo de ativação da polimerização e envelhecimento acelerado em algumas propriedades de cimentos resinosos / Effects of polymerization activation protocol and accelerated aging in some resin cements properties

AUTOR(ES)
DATA DE PUBLICAÇÃO

2010

RESUMO

The study aimed to evaluate the effects of curing protocol and accelerated aging on some properties of dual-cure resin cements. Additionally, the effects of different ambient temperature and aging on the working and setting times were investigated when cements were self-cured only. Properties evaluated were degree of conversion as determined by FTIR-ATR spectroscopy, Knoop microhadness as expressed by KHN, and tensile strength as expressed in MPa. Working time and setting time were determined by an oscilating rheometer with controlled temperature stage at either 24oC or 37oC. Accelerated aging was performed by storing the original product kits in an oven at 37oC for 12 weeks after initial testing had been executed. Different curing protocols were established in 3 levels. Cements were manipulated according to the manufacturers instructions and light-activated immediately (control), light-activated after 10 minutes delay of self-curing in the dark (Exp 1), or simply allowed to self-cure for 15 minutes in the dark (Exp 2). Properties were evaluated according to the different curing protocol and both before and after aging. Exclusively self-curing cement was used as control product when appropriate. The results can be summarized in some aspects of interest. The working time and setting time of all products were significantly affected by temperature and aging (p<0.05). Increased temperature resulted in shorter working time and setting time. The effects of aging were material dependent. Some products presented reduced working and setting times, while others behave otherwise, regardless of the temperature. Curing mode and aging significantly affected the properties of the cements (p<0.05). In general, the degree of conversion increased with time after light-activation. The curing delay for 10 minutes caused alterations in the degree of conversion, regardless of aging, for some products, but not all. Aging affected the curing kinectics and general properties of all cements. Some materials did not present sufficient cure after aging. Properties varied widely according to curing protocol and product. Aging was the variable that most affected the products and the most relevant regarding the clinical use of the materials. Some products were deemed improper for clinical use after accelerated aging.

ASSUNTO(S)

cimento resinoso dual mechanical properties setting time degree of conversion tempo de presa aging envelhecimento propriedades mecânicas working time grau de conversão polymerization mode modo de polimerização dual-cured resin cement tempo de trabalho

ACESSO AO ARTIGO

Documentos Relacionados