Efecto de la Profundidad sobre la Soldabilidad de Aceros Ferríticos en Ambientes Simulados Unidos por Soldadura Húmeda

AUTOR(ES)

López, Fernando Macías, Vidaurri, Luciano Eliezer Ramírez, Dávila, Jorge Leobardo Acevedo, Hdz-García, Héctor M., Hernández-Rodríguez, A., Mondragon, J. Jorge Ruiz

FONTE

Soldag. insp.

DATA DE PUBLICAÇÃO

2016-06

RESUMO

Abstract The objective of this work is to evaluate the influence of depth variation on multipass V-groove weld metal properties. Commercial base metal and covered electrodes (ASTM A36 and E7014) and four different conditions were used to perform the wet welds at 10, 20, 30 and 40 m depth. A pressurized chamber with 30 atmospheres capacity filled with water was used to simulate the depth. A certified dive welder was used to perform the welds. The properties in transverse cross-sections, Charpy V-notch tests, macro etching tests and tensile tests were determined for correlation. Mechanical tests showed better properties in the samples extracted from the 20m depth condition.

Documentos Relacionados

• Efecto del procedimiento de soldadura sobre las propiedades de uniones soldadas de aceros microaleados para cañería
• Modelado numérico del proceso de soldadura por fricción agitación en aceros inoxidables
• Efecto del procedimiento de soldadura por FSW en la evolución temporal de las propiedades en uniones de AA 7075-T651
• Efecto de los parámetros de soldadura sobre la microestructura de recargues nanoestructurados base hierro depositados por FCAW-S
• Efecto de la composición sobre el comportamiento frente a la corrosión de aceros inoxidables austeníticos y martensíticos