Determinação do perfil térmico em amostras de aço AISI M35 imersas em plasma
AUTOR(ES)
Nierlly Karinni de Almeida Maribondo Galvão
DATA DE PUBLICAÇÃO
2007
RESUMO
The heat transfer between plasma and a solid occurs mostly due the radiation and the collision of the particles on the material surface, heating the material from the surface to the bulk. The thermal gradient inside the sample depends of the rate of particles collisions and thermal conductivity of the solid. In order to study that effect, samples of AISI M35 steel, with 9,5 mm X 3,0 mm (diameter X thickness) were quenched in resistive furnace and tempereds in plasma using the plane configuration and hollow cathode, working with pressures of 4 and 10 mbar respectively. Analyzing the samples microstructure and measuring the hardness along the transversal profile, it was possible to associate the tempered temperature evaluating indirectly the thermal profile. This relation was obtained by microstructural analyzes and through the hardness curve x tempered sample temperature in resistive furnace, using temperatures of 500, 550, 600, 650 and 700C. The microstructural characterization of the samples was obtained by the scanning electron microscopy, optic microscopy and X-ray diffraction. It was verified that all samples treated in plasma presented a superficial layer, denominated affected shelling zone, wich was not present in the samples treated in resistive furnace. Moreover, the samples that presented larger thermal gradient were treated in hollow cathode with pressure of 4 mbar
ASSUNTO(S)
cátodo oco plasma hollow cathode thermal gradient m35 steel aço m35 engenharia de materiais e metalurgica plasma gradiente térmico
Documentos Relacionados
- Tratamento térmico superficial do aço AISI M2 via laser de CO2.
- Cementação sob plasma à baixa temperatura do aço inoxidável austenítico AISI 316L e do aço inoxidável duplex AISI F51
- Nitrocarbonetação por plasma, em potencial flutuante, de aço inoxidável austenítico AISI 304
- Análise da influência de tratamento térmico na resistência à corrosão-erosão do aço inoxidável AISI 304
- Caracterização das superfícies e regiões interfaciais de filmes nanométricos de TiN/Ti/Aço AISI M2 nitretado a plasma