Detailed crystallization study of co-precipitated Y1.47Gd1.53Fe5O12 and relevant magnetic properties
AUTOR(ES)
Serra, Rogério Arving, Ogasawara, Tsuneharu, Ogasawara, Angélica Soares
FONTE
Química Nova
DATA DE PUBLICAÇÃO
2007
RESUMO
The crystallization process of co-precipitated Y1.5Gd1.5Fe5O12 powder heated up to 1000 ºC at rate of 5 °C min-1 was investigated. Above 810 ºC crystalline Y1.47Gd1.53Fe5O12 was obtained with a lattice parameter of 12.41 Å and a theoretical density of 5.84 g cm-3. Dry pressed rings were sintered at 1270 and 1320 ºC, increasing the grain-size from 3.1 to 6.5 µm, the theoretical density by 87.6 to 95.3% and decreasing Hc from 2.9725 to 1.4005 Oe. Additionally, Hc increased when the frequency of the hysteresis graph varied from 60 Hz to 10 kHz, the curie temperature was 282.4 ºC and Ms equalled 9.25 emu g-1 (0.17 kG) agreeing well with the Bs-value of the hysteresis graph and literature values.
Documentos Relacionados
- Dry reforming of methane at moderate temperatures over modified Co-Al Co-precipitated catalysts
- Structural, Morphological and Magnetic Properties of FeCo-(Fe,Co)3O4 Nanocomposite Synthesized by Proteic Sol-Gel Method Using a Rotary Oven
- Structural and magnetic properties of the half-ferromagnetic Co2+x+yMn1-xAl1-y alloys
- Magnetic and Electrical Properties of MnxCu1-xFe2O4 Ferrite
- Magnetic properties of Pr-Fe-Co-B bonded HDDR magnets with alloying additions