Desenvolvimento e uso do compósito de Nb2O5|Cu como revestimento aplicado por aspersão térmica sobre o aço AISI 1020 para proteção contra a corrosão pelo solo em estruturas enterradas
AUTOR(ES)
Regis Junior, Oscar, Silva, José Maurílio da, Portella, Kleber Franke, Paredes, Ramon Sigifredo Cortes
FONTE
Quím. Nova
DATA DE PUBLICAÇÃO
2012
RESUMO
An Nb2O|Cu corrosion-resistant coating was developed and applied onto AISI 1020 steel substrate by Powder Flame Spray. A galvanostatic electrochemical technique was employed, with and without ohmic drop, in four different soils (two corrosively aggressive and two less aggressive). Behavior of coatings in different soils was compared using a cathodic hydrogen reduction reaction (equilibrium potential, overvoltage and exchange current density) focusing on the effect of ohmic drop. Results allow recommendation of Nb2O5|Cu composite for use in buried structure protection.
Documentos Relacionados
- Avaliação da resistência à corrosão do aço AISI 420 depositado por processos variados de aspersão térmica
- Proteção contra a corrosão com revestimentos de zinco e aluminio depositados por aspersão termica
- Estudo das características de revestimentos poliméricos aplicados por aspersão térmica para proteção contra desgaste e corrosão de substratos metálicos
- Estudo da corrosão de aço AISI 1020 em meio de petróleo
- Adição de plastificante à polianilina sintetizada quimicamente e avaliação dos filmes plastificados como proteção contra a corrosão do aço AISI 1010