Desempenho físico-químico de metais e estruturas de concreto de redes de distribuição de energia: estudo de caso na região de Manaus
AUTOR(ES)
Portella, Kleber Franke, Garcia, Carlos Mario, Vergés, Giseli Ribeiro, Joukoski, Alex, Freire, Karla Regina Rattmann, Corrêa, Alcyr de Pinho
FONTE
Química Nova
DATA DE PUBLICAÇÃO
2006-07
RESUMO
The influence of natural aging furthered by atmospheric corrosion of parts of electric transformers and materials, as well as of concrete poles and cross arms containing corrosion inhibitors was evaluated in Manaus. Results for painted materials, it could showed that loss of specular gloss was more intensive in aliphatic polyurethane points than in acrylic polyurethane ones. No corrosion was observed for metal and concrete samples until 400 days of natural aging. Corrosion in steel reinforcement was noticed in some poles, arising from manufacturing faults, such as low cement content, water/cement ratio, thin concrete cover thickness, etc. The performance of corrosion inhibitors was assessed by many techniques after natural and accelerated aging in a 3.5% saline aqueous solution. The results show the need for better chemical component selection and its concentration in the concrete mixture.
Documentos Relacionados
- Desempenho físico-químico e mecânico de concreto de cimento Portland com borracha de estireno-butadieno reciclada de pneus
- Estudo fisico-quimico de polietileno glicol com agua e sorventes aromaticos
- Estudo botânico, fitoquímico e fisico-químico de Euphorbia hirta L. (Euphorbiaceae)
- Estudo físico-químico da interface eletrólito polimérico/nanotubos de carbono.
- Síntese e caracterização de compósito polipirrol/botriosferana : um estudo físico-químico