Decomposição térmica de espumas de poliuretano para fabricação de vitrocerâmica celular de Li2O-ZrO2-SiO2-Al2O3 (LZSA)

AUTOR(ES)

Silveira, Cristian Berto da, Escobar, Jairo A., Quintero, Miguel W., Sousa, Eliandra de, Moraes, Elisângela Guzzi de, Oliveira, Antônio Pedro Novaes de, Rambo, Carlos Renato, Hotza, Dachamir

FONTE

Química Nova

DATA DE PUBLICAÇÃO

2007-10

RESUMO

Characterization of the thermal decomposition of polyurethane (PUR) foams was performed by Fourier-transformed infrared (FT-IR) spectroscopy and thermogravimetric analysis (TGA). Three main weight loss paths were observed by TGA, the residue being lower than 3 wt.% for 3 different PUR foams analyzed. FT-IR spectra indicated CO2, CO, NH3 and isocyanides as main decomposition products. PUR foams of different cell sizes were immersed in a slurry of the parent glass ceramic of composition Li2O-ZrO2-SiO2-Al 2O3 (LZSA) and submitted to heat treatment. The LZSA cellular glass ceramics obtained after sintering and crystallization resembled the original morphology of the PUR foams.

Documentos Relacionados

• Processamento e caracterização de espumas vitrocerâmicas do sistema Li2O-ZrO2-SiO2-Al2O3 (LZSA) produzidas por gelcasting
• Cristalização de superfície em vidro do sistema Li2O–ZrO2–SiO2–Al2O3
• Espumas vítreas do sistema Li2O-ZrO2-SiO2-Al2O 3 produzidas pelo processo gelcasting
• Obtenção e caracterização de laminados vitrocerâmicos do sistema Li2O-ZrO2-Si02-Al2O3 (LZSA) por manufatura de obejtos laminados (LOM)
• Crystallization Mechanism and Kinetics of BaO-Li2O-ZrO2-SiO2 Glasses