Crack propagation under variable amplitude loading
AUTOR(ES)
Abdelkader, Miloudi, Mokhtar, Zemri, Mohamed, Benguediab, Mohamed, Mazari, Abdelwaheb, Amrouche
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
05/07/2013
RESUMO
Experience shows that a damage induced by a given cycle is dependent on the loading history. In this regard, the objective of this paper is to study and describe the phenomenology of the loading history on crack propagation. Different loading configuration has been considered for fatigue crack propagation of XC38 steel; overload cycles followed by underload and vice versa were considered during propagation. Measure of crack opening has been made using compliance method. It is shown that the main parameters which cause retardation are the residual compressive stresses and the crack closure. The finite element modeling is used to calculate the evolution of residual stress profiles before and after application of the overload-underload cycle. It corroborates the hypotheses on the mechanisms behind, including those proposed on the residual stresses at the crack tip.
Documentos Relacionados
- Crack propagation under constant amplitude loading based on an energetic parameters and fractographic analysis
- Modelagem Computacional da PropagaÃÃo de Trincas em Vigas de Pontes de AÃo sob Carregamento CÃclico de Amplitude VariÃvel
- On the crack propagation analysis of rock like Brazilian disc specimens containing cracks under compressive line loading
- Dynamic crack propagation of granite subjected to biaxial confining pressure and blast loading
- FATIGUE CRACK PROPAGATION IN ARBITRARY 2D GEOMETRIES UNDER COMPLEX LOADING.