Copper/Iron Brake Friction for Military Aircraft Application
AUTOR(ES)
Santos, Thiago Duque Estrada da Silva, Regiani, Inácio, Rocha, Roberta Jachura, Rocco, José Atílio Fritz Fidel
FONTE
J. Aerosp. Technol. Manag.
DATA DE PUBLICAÇÃO
03/05/2018
RESUMO
ABSTRACT: The present study assesses the influence of non-metallic constituents and manufacturing parameters, such as compaction pressure and sintering temperature, to produce a metal matrix composite (MMC) of copper/iron, based on the brake disc of aircraft AT-29 SuperTucano. The samples were produced with six different compositions, by varying the amount of abrasive particles (quartz and zirconia silicate) and the solid lubricant (graphite), with one of the compositions manufactured without the addition of graphite. The compaction pressures were 210 and 420 MPa, with sintering temperatures of 950 °C and 1050 °C in a furnace with controlled atmosphere of argon + 10% H2. After sintering, the effectiveness of the sintering process was evaluated through the apparent density (Archimedes's method), Brinell and Vickers hardness, and the microstructure by Scanning Electron Microscopy (SEM). The sintering process was severely affected by the solid lubricant (graphite): its reduction resulted in a density increase near 18%, and the hardness of the compound up to 62%. The hardness values demonstrated significant variation with compaction pressure, with a pronounced effect on compounds with less non-metallic elements. SEM analysis demonstrated that not only graphite, but also the ceramic particles affected the sintering process through the agglomeration of inclusions into the metal-metal interface. The samples without graphite exhibited almost the same value of pores after sintering, regardless of the compaction pressure, indicating that the graphite content affects directly the sintering process, regardless of the compaction pressure.
Documentos Relacionados
- Application of a Greedy Algorithm to Military Aircraft Fleet Retirements
- Information and knowledge models supporting brake friction material manufacturing
- Finite Element Analysis of Pilot’s Helmet Design Using Composite Materials for Military Aircraft
- The effects of porosity in friction performance of brake pad using waste tire dust
- Effect of Rockwool and Steel fiber on the Friction Performance of Brake Lining Materials