Composition, Elastic Property and Packing Efficiency Predictions for Bulk Metallic Glasses in Binary, Ternary and Quaternary Systems
AUTOR(ES)
Borja Soto, Carlos Ernesto, Figueroa Vargas, Ignacio Alejandro, Fonseca Velázquez, José Ramón, Lara Rodriguez, Gabriel Ángel, Verduzco Martínez, Jorge Alejandro
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
08/03/2016
RESUMO
The results of database based on the efficiency packed model for metallic glasses. The database contains the atomic radii information as well as elastic properties of the most commonly used alloying elements, permitting composition, packing efficiency and elastic property predictions to be made for binary, ternary and quaternary bulk metallic glasses. Twenty different alloys per system (binary, ternary and quaternary) experimentally reported in the literature were compared with those estimated by the database. Comparison charts and diagrams showed good agreement between the composition predictions and those reported from the experimentally processed metallic glasses. The elastic properties predictions could be used to elaborate Blackman diagrams in order to know, in advance, the intrinsic toughness that the investigated alloys might present. The database is intended for designing bulk metallic glasses. Finally, some quaternary alloys were experimentally produced based on the prediction obtained with the database, showing a glassy phase. The microhardness values obtained experimentally of the Zr57.52Ag10.62Al10.62Co21.24, Zr57.19Al10.7Ni10.7Cu21.41 and Hf60.22Al9.95Cu9.95Ni19.89alloys, are 3.8, 4.0 and 3.6 GPa, respectively. The Young´s modulus calculated using microhardness values (E/Hv = 20) are closed to the values obtained by the "mixing rules".
Documentos Relacionados
- The Effect of Composition, Temperature and Post-Irradiation Curing of Bulk Fill Resin Composites on Polymerization Efficiency
- Modelagem de equilíbrio líquido-líquido, líquido-vapor e líquido-líquido-vapor para sistemas binários, ternários, quaternários e pseudo-quaternários, envolvendo a produção de biodiesel
- PHASE RELATIONS IN SYSTEMS COMPRISING BROMINE AND QUATERNARY AND TERNARY ALKYL AMMONIUM BROMIDES OR CHLORIDES
- Desenvolvimento de um processo para a produção de peças metálicas vítreas
- Influence of Small Content Elements Additions on the Glass Forming Ability of Zr-based Bulk Metallic Glasses Alloys