Cold metal transfer welding of AA1050 aluminum thin sheets
AUTOR(ES)
İrizalp, Alaattin Ozan, Durmuş, Hülya, Yüksel, Nilay, Türkmen, İlyas
FONTE
Matéria (Rio J.)
DATA DE PUBLICAÇÃO
2016-09
RESUMO
ABSTRACT This study was aimed to investigate the welding parameters on mechanical behavior of 2 mm thick AA1050 sheet materials joined by cold metal transfer (CMT) method. Macro structural examination showed that decreasing heat input decreased the pore size in the weld metal. Tensile test was applied and failure occurred in heat affected zone of aluminum sheet metal. Maximum tensile strength was found in the sample with minimum heat input. Heat affected zone was observed explicitly in the sample produced with the maximum heat input. Decreasing joint gap affected the bending strength positively. Bending strength was found superior with maximum bonding line length.
Documentos Relacionados
- Welding of AA1050 aluminum with AISI 304 stainless steel by rotary friction welding process
- Experimental Determination of Temperature During Rotary Friction Welding of AA1050 Aluminum with AISI 304 Stainless Steel
- Metal transfer in the aluminum gas metal arc welding
- Efeito de tratamentos de modificação da superfície na resistência à corrsão do alumínio 1050
- Caracterização microestrutural dos alumínios comerciais AA1100, AA1050 e AA1070 e do alumínio superpuro AA1199