Bond strength durability of self-etching adhesives and resin cements to dentin
AUTOR(ES)
Chaves, Carolina de Andrade Lima, Melo, Renata Marques de, Passos, Sheila Pestana, Camargo, Fernanda Pelógia, Bottino, Marco Antonio, Balducci, Ivan
FONTE
Journal of Applied Oral Science
DATA DE PUBLICAÇÃO
2009-06
RESUMO
OBJECTIVES: To evaluate the microtensile bond strength (µTBS) of one- (Xeno III, Dentsply) and two-step (Tyrian-One Step Plus, Bisco) self-etching adhesive systems bonded to dentin and cemented to chemically cured (C&B Metabond) or light-cured paste of a dual-cure resin cement (Variolink II, Ivoclar) within a short (24 h) and long period of evaluation (90 days). MATERIAL AND METHODS: Forty recently extracted human molars had their roots removed and their occlusal dentin exposed and ground wet with 600-grit SiC paper. After application of one of the adhesives, the resin cement was applied to the bonded surface and a composite resin block was incrementally built up to a height of 5 mm (n=10). The restored teeth were stored in distilled water at 37ºC for 7 days. The teeth were then cut along two axes (x and y), producing beam-shaped specimens with 0.8 mm² cross-sectional area, which were subjected to µTBS testing at a crosshead speed of 0.05 mm/min and stressed to failure after 24 h or 90 days of storage in water. The µTBS data in MPa were subjected to three-way analysis of variance and Tukey's test (α= 0.05). RESULTS: The interaction effect for all three factors was statistically significant (three-way ANOVA, p<0.001). All eight experimental means (MPa) were compared by the Tukey's test (p<0.05) and the following results were obtained: Tyrian-One Step Plus /C&B/24 h (22.4±7.3); Tyrian-One Step Plus /Variolink II/24 h (39.4±11.6); Xeno III/C&B/24 h (40.3±12.9); Xeno III/Variolink II/24 h (25.8±10.5); Tyrian-One Step Plus /C&B/90 d (22.1±12.8) Tyrian-One Step Plus/VariolinkII/90 d (24.2±14.2); Xeno III/C&B/90 d (27.0±13.5); Xeno III/Variolink II/90 d (33.0±8.9). CONCLUSIONS: Xeno III/Variolink II was the luting agent/adhesive combination that provided the most promising bond strength after 90 days of storage in water.
Documentos Relacionados
- Do the origins of primary teeth affect the bond strength of a self-etching adhesive system to dentin?
- Effect of refrigeration on bond strength of self-etching adhesive systems
- Can previous acid etching increase the bond strength of a self-etching primer adhesive to enamel?
- Localized mechanics of dentin self-etching adhesive system
- Bond strength and morphology of enamel using self-etching adhesive systems with different acidities