Bond strenght between resin cements and zirconia / Resistência de união entre cimentos resinosos e zircônia
AUTOR(ES)
Juan Rommel Medina Valdivia
FONTE
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia
DATA DE PUBLICAÇÃO
18/08/2011
RESUMO
The aim of this study was to evaluate the shear bond strength of resin cements to the yttria stabilized tetragonal zirconia (NobelProceraTM Zirconia) subjected to mechanical and chemical surface treatments. The cements used were: a self-etching resin cement with chemical polymerization Multilink (Ivoclar - Vivadent) associated to the Metal / Zirconia Primer (Ivoclar - Vivadent) and self-adhesive resin cement with chemical and dual polymerization RelyX U100 (3M-ESPE) associated to the adhesive Single Bond Plus Adper 2 (3M-ESPE). Using 40 cylinders of zirconia (3.5 mm diameter) were performed 120 trials (n = 40 for each cement). For each cement, cylinders were divided into four groups (n = 10) based on the surface treatment rated: 1 - untreated, 2 - bonding agent (primer or adhesive) 3 air abrasion with 50µm aluminum oxide, 4 - combination of air abrasion and bonding agent. The application of resin cement was performed using a teflon matrix with a central hole 3.5 mm in diameter and 3.0 mm deep. After application of each cement in the four surface conditions, the specimens were stored in deionized water at 37 ° C for 24 hours and tested for shear bond strength. Results were analyzed with an ANOVA Two Criteria and Tukey\ s test (p <0.05). Without surface treatment, chemical RelyX U100 (5.52 MPa) and dual (6.53 MPa) had better behavior than Multilink Cement (0.76). The combination of air abrasion and bonding agent improved the bond strength values for Multilink (7.68 MPa) and for RelyX U100 dual (10.26 MPa), this one superior to all other groups. The association of Adper Single Bond 2 and RelyX U100 Plus without air abrasion, should be contraindicated.
ASSUNTO(S)
cimentos de resina resin cements resistência ao cisalhamento shear bond strength zircônio zirconium
Documentos Relacionados
- Conventional and self-adhesive resin cements : filler particles characterization, ultramicromorphology and dentin-resin bond strenght
- Avaliação in vitro da resistência adesiva e degradação da interface de união entre cimentos resinosos e uma cerâmica aluminizada tratada internamente com laser
- Resistência de união entre o titânio fundido e cimentos resinosos, comparada com a de uma liga de níquel-cromo.
- Estudo da resitência de união de cimentos resinosos à cerâmicas à base de dislicato de lítio, leucita e zircônia
- Avaliação da radiodensidade de cimentos resinosos