Avaliação do efeito da concentração de carbonato na eletrodeposição de cobre sobre discos de aço-carbono
AUTOR(ES)
Silva, Angélica Inês Ferreira da, Afonso, Júlio Carlos, Sobral, Luis Gonzaga Santos
FONTE
Química Nova
DATA DE PUBLICAÇÃO
2008
RESUMO
Mild steel blankets were covered with electrolytic copper thin layer, from cyanide bath, being evaluated the influence of the carbonate concentration in the physiochemical properties of those deposits. The cell voltage decreased as the current intensity decreased, but the adherence of the deposit was not enhanced, showing that the increment of carbonate concentration causes substantial problems. Chemical solubilization reactions of air-bearing carbon dioxide and oxidation of free cyanide ions through dissolved oxygen evolved in the anodic processes contribute to the copper plating to occur in an inefficient way. The best optimal conditions require a carbonate concentration below 50 g L-1.
Documentos Relacionados
- EXTRATO DE HIBISCO-COLIBRI COMO INIBIDOR VERDE DE CORROSÃO DO AÇO-CARBONO EM ÁCIDO SULFÚRICO
- Análise dos estágios iniciais da corrosão do aço-carbono e aço patinável expostos em ambiente marinho-industrial e rural
- Ação inibidora de extratos da semente do mamão papaia na corrosão do aço-carbono 1020 em HCL 1 mol L-1
- INIBIÇÃO À CORROSÃO DE AÇO-CARBONO EM MEIO SALINO PELO HETEROCICLO ISATINA VEICULADO EM MICROEMULSÕES
- Obtenção e caracterização de revestimentos protetores a base de silanos e sua ação combinada com tintas na proteção ao aço-carbono