AVALIAÇÃO DO DESEMPENHO DE UMA FASE SENSORA DE POLIURETANO POR MEIO DA ENERGIA DE GIBBS DE SOLVATAÇÃO E ESPECTROSCOPIA DE INFRAVERMELHO PARA DETERMINAÇÃO DE TOLUENO EM ÁGUA

AUTOR(ES)

Souza, Juliana D. C., Azevedo Júnior, Rogerio V. de, Vinhas, Glória M., Lima, Nathalia B. D., Brito, Andréa M. S. S.

FONTE

Quím. Nova

DATA DE PUBLICAÇÃO

2018-04

RESUMO

A novel sensing phase of polyurethane was predicted by quantum chemical calculations as capable of detecting toluene, with the experimental results revealing a limit of detection of 1.4 mg L-1 in the determination of toluene in water samples. The quantum chemical computational strategy was validated by assessing the impact of the polymer matrix sensing phases polyvinyl chloride (PVC), polydimethylsiloxane (PDMS), and polyisobutylene (PIB), as solvents, on the Gibbs energy of solvation of the organic contaminants toluene, benzene, chlorobenzene and ethylbenzene. Computational results for the set studied indicate that the limit of detection of contaminants for each polymeric matrix correlated well with the Gibbs energy of solvation. As such, the computational methodology was employed to assess the potential applicability of polyurethane matrices on the determination of toluene as a contaminant in water, with positive results. Analyzes were then carried out experimentally by mid-infrared spectroscopy. Finally, experiments revealed good regenerative capacity of polyurethane, further adding to the usefulness of the technique here advanced.

Documentos Relacionados

• FASE SENSORA DE POLI(CLORETO DE VINILA) NA DETECÇÃO DE 17β-ESTRADIOL EM MEIO AQUOSO UTILIZANDO ESPECTROSCOPIA NO INFRAVERMELHO MÉDIO E QUIMIOMETRIA
• Calibração multivariada para determinação de componentes de forrageiras por meio de espectroscopia de infravermelho próximo (NIRS).
• Determinação das propriedades das forrageiras por meio de espectroscopia de infravermelho próximo (NIRS).
• Espectroscopia de infravermelho na determinação da textura do solo
• Avaliação por espestroscopia no infravermelho da microestrutura de poliuretano baseado em resina polibutadiênica hidroxilada