Avaliação da tensão superficial do PVB e da PA-6. / Evaluation of surface tension of poly(vinyl butyral) and nylon-6.

AUTOR(ES)
DATA DE PUBLICAÇÃO

2008

RESUMO

In the Rheology and Polymer Processing Laboratory of Escola Politécnica of the University of São Paulo, Polyamide-6 / poly(vinyl butiral) film blends have been studied as an alternative for the recycling of post-consumption laminated glasses. The mechanical properties of these blends were studied and explained in light of their morphology. The morphology of polymer blends strongly depends on the rheological behavior of the blend and on the interfacial tension between the polymers forming the blend. In the case of Poliamide-6 (PA-6)/poly(vinyl butiral) (PVB) film blends, the interfacial tension depends on the plasticizer concentration present in PVB film. However, to our knowledge neither the PA-6/PVB film interfacial tension nor the surface tension of PVB film at temperatures above softening temperatures have been evaluated. In this work, the surface tension of poly(vinyl butyral) and polyamide was evaluated using the pendant drop method. Also it was tried to evaluate the surface tension of PVB film as a function of plasticizer content. The surface tension values obtained were in the same range as the ones obtained for other molten polymers: the surface tension decreases with increasing temperature (for temperatures ranging from 240 to 260°C). However, the value of PVB film surface entropy ((d/dT) where is the surface tension and T is the temperature) was much larger than values reported for other molten polymers. This result was attributed to thermal stability of PVB film during the surface tension measurement. The drops of PVB film after surface tension analysis were examined for any change in their functional groups using infrared spectroscopy (FITIR), ultraviolet-visible spectroscopy (UV/VIS), electron spectroscopy for chemical analysis (XPS/ESCA) and thermogravimetric analysis (TG). The results showed that changes in the chemical structure of PVB film occur during surface tension measurement. First, the plasticizer within the PVB film evaporates and, then, the PVB suffers reduction of polar units and creation of C=C bonds. The surface tension of PA-6 was evaluated for temperatures of 250 and 260°C. The PA-6 remained stable during tests.

ASSUNTO(S)

poli (vinil butiral) pendant drop method método da gota pendente tensão superficial poly (vinyl butiral) poliamida-6 surface tension nylon-6

ACESSO AO ARTIGO

Documentos Relacionados