Analysis of the Crystallographic Microtexture of a UNS S32205 and a UNS S32304 Duplex Stainless Steels After Cold Rolling and Heat Treatment
AUTOR(ES)
Gonçalves, Karina Aparecida Martins Barcelos, Santos, Dagoberto Brandão, Oliveira, Tarcísio Reis de
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
26/07/2018
RESUMO
Samples of duplex stainless steel 32205 (standard duplex) and 32304 (lean duplex) were investigated in the as-received state, cold rolling (with thickness reduction of 64 % and 62 % respectively) and after annealing at 1055ºC for 20 s soaking. Crystallographic microtexture was obtained via Electron BackScatter Diffraction (EBSD) technique. The results showed that the crystallographic microtexture of ferrite phase in the as-received, cold rolled and annealed condition were more intense in alpha fiber=<011> // RD and tetha fiber. The austenite microtexture was shown to be, for all conditions, mainly composed by Brass component.
Documentos Relacionados
- Tensile properties of duplex UNS S32205 and lean duplex UNS S32304 steels and the influence of short duration 475 ºC aging
- Double Kinetics of Intermetallic Phase Precipitation in UNS S32205 Duplex Stainless Steels Submitted to Isothermal Heat Treatment
- Effect of Warm Rolling on the Corrosion and Mechanical Properties of UNS S32205 Duplex Stainless Steel
- Martensitic transformation induced by cold deformation of lean duplex stainless steel UNS S32304
- Efeitos de envelhecimentos em baixas temperaturas nas propriedades mecânicas e resistência à corrosão dos aços duplex e lean duplex UNS S32205 e UNS S32304