Amplitude-Dependent Internal Friction Study of Fatigue Deterioration in Carbon Fiber Reinforced Plastic Laminates

AUTOR(ES)

Nishino, Yoichi, Kawaguchi, Ryota, Tamaoka, Satoshi, Ide, Naoki

FONTE

Mat. Res.

DATA DE PUBLICAÇÃO

07/06/2018

RESUMO

The amplitude-dependent internal friction in carbon fiber reinforced plastic (CFRP) laminates subjected to fatigue cycling has been measured and analyzed to convert into the plastic strain of the order of 10-8 as a function of effective stress. The microplastic flow indeed occurs in the stress range three orders of magnitude lower than the failure stress, and the stress-strain curves tend to shift to a lower stress as the number of cycles increases, thus indicating a decrease in the CFRP strength. The microflow stress at the plastic strain of 1×10-8 keeps a constant value of about 0.4 MPa in the range less than 103 cycles but then decreases gradually, whereas the Young's modulus evaluated from the resonant frequency is almost constant up to 104 cycles where only transverse cracks are found. Thus we can successfully detect the onset of fatigue deterioration by means of the amplitude-dependent internal friction.

Documentos Relacionados

• Fracture morphology of carbon fiber reinforced plastic composite laminates
• Measurement of Strain-Amplitude Dependent Internal Friction with Torsion Pendulum and Vibration Reed Methods
• Fatigue damage mechanism and failure prevention in fiberglass reinforced plastic
• Multi-scale representation of plastic deformation in fiber-reinforced materials: application to reinforced concrete
• Mechanical performance of carbon-epoxy laminates. Part II: quasi-static and fatigue tensile properties